Título :	MORTERO COMPUESTO CON MATERIAL DE CAMBIO DE FASE (PCM) PARA PANELES PREFABRICADOS LIGEROS
Sustentante:	Juan Carlos Ledesma García Ángel Jiménez Loredo
Palabras clave :	INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS
Fecha de publicación :	nov-2018
metadata.dc.degree.department:	Facultad de Ingeniería
metadata.dc.degree.name:	Ingeniería Civil
Descripción :	El presente trabajo de tesis expone la utilización de material cambio de fase (PCM) y material ligero (pomacita) en mezclas de mortero, en base de cemento portland, con el objetivo de mejorar las condiciones térmicas y mecánicas bajo esfuerzos de compresión y flexión en los morteros y con esto reducir la demanda energética en el sector residencial. Se realizó una primera mezcla de control con una relación de cemento-arena 1:3 y una fluidez de 110% +/- 5%, en base a ésta se elaboró una segunda mezcla sustituyendo por material ligero. La tercer y cuarta mezcla fue una relación 1:2 cemento-arena variando la cantidad de PCM y cambiando la proporción de la mezcla de control. La quinta y sexta mezcla fue una relación 1:1 cemento-arena y variando la cantidad de PCM y cambiando las proporciones de la mezcla de control. De cada dosificación se realizaron 10 probetas para ensayes a esfuerzos de compresión, y 10 para ensayes a esfuerzos de flexión con la finalidad de identificar las muestras con las mejores propiedades mecánicas. Adicionalmente, se realizaron 5 probetas para las dosificaciones que contienen únicamente PCM para obtener el comportamiento térmico de las muestras. Para todas las mezclas se obtuvo la fluidez, esfuerzos a compresión y a flexión en los morteros. Los resultados demuestran que una de las mezclas de mortero ensayada obtuvo una notable resistencia bajo esfuerzos de compresión y una mejora bajo esfuerzos de flexión. Por lo tanto, de acuerdo a los resultados se presume que el PCM podría representar una alternativa como agregado en paneles prefabricados. The present work of this thesis is showing the usage of phase change material (PCM) and lightweight material (pumice) that are mixed with mortars, which contains Portland cement to improve thermal and mechanical behavior. The mixes are tested under compression and bending stresses to cut down the energy demand in the construction industry. Six mixes were tested with different amounts of material and proportions of PCM and lightweight material. For such effect, the first mix has a ratio 1:3 cement–sand and fluidity of 110% +/- 5%. The second one, it was replaced lightweight material instead of sand. The third and fourth mixtures had a ratio 1:2 cement-sand which was changed the relation and these mixtures had a variety of amounts of PCM. The fifth and sixth mixtures had a ratio 1:1 cement – sand, which also changed the relation and their testes had a variety of amounts of PCM. Ten samples were made for every mixture to test under compression stresses and ten samples to test under bending stresses to find the best mixtures, which might have good mechanical properties. Additionally, five samples were made just for the mixtures which contain PCM material to test them and identify the thermal properties. All the samples were tested under compression stresses and bending stresses. The results show that one of the mortar mixtures got a remarkable compression stress and a better bending stress. Therefore according to the results it is presumed that the PCM could represent a good alternative of material to be used in prefabricated panels.
URI :	http://ri-ng.uaq.mx/handle/123456789/1500
Otros identificadores :	PCM Material ligero Mortero Propiedades mecánicas Conductividad térmica PCM Lightweight material Mortar Mechanical properties Thermal conductivity.
Aparece en las colecciones:	Ingeniería Civil

Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.